双马来酰亚胺(BMI)胶粘剂以其优异的性能在航空航天领域中得到了广泛应用,尤其大量应用于BMI树脂基复合材料整体化成型和高性能结构件制造过程中。对国内外BMI胶粘剂的研究、发展现状做了简要介绍;重点介绍了采用热塑性树脂、橡胶弹性体、环氧树脂、氰酸酯树脂和无机填料等改性方法制备BMI胶粘剂的研究进展及改性过程中存在的问题;最后对BMI胶粘剂发展前景进行了展望,并根据发展需要提出了五个发展方向,为以后BMI胶粘剂的进一步研究及应用提供参考。
Bismaleimide (BMI) adhesives had been widely used in aerospace field with their excellent properties,especially in the process of integrated molding and manufacturing of high performance structural parts of bismaleimide resin matrix composites.A brief introduction to the research and development of the bismaleimide adhesive at home and abroad was gived.The research progress and problems in the preparation of the bismaleimide adhesives by thermoplastic resin,rubber elastomer,epoxy resin,cyanate resinand inorganic filler were mainly introduced.Finally,the development prospect of the BMI adhesives was expected,and put forwarded five development directions according to the development needs.It provided reference for further research and application of bismaleimide adhesives.
[1] Agag T,Vietmeier K,Chernykh A,et al.Side-chain type benzoxazine-functional cellulose via click chemistry[J].J Appl Polym Sci,2012,125(2):1346-1351.
[2] Yao L U,Duan Y X,Liang Z Y.Studies on rheological behaviors of bismaleimide resin system for resin transfer molding[J].Chin J Aeronautics,2002,15(3):181-185.
[3] 董金虎.绝缘导热高分子复合材料研究现状[J].广州化工,2012(6):14-18.
[4] 王汝敏,舒武炳.韧性双马来酰亚胺树脂基复合材料的研究[J].纤维复合材料,2000,3(30):53-56.
[5] 杜善义.先进复合材料与航空航天[J].复合材料学报,2007,24(1):1-12.
[6] 曹魏,熊艳丽,凌辉等.耐高温双马树脂体系[J].宇航材料工艺,2011,41(2):61-63.
[7] Karbhari V M,Xian G J.Hygrothermal effects on high VF pultruded unidirectional carbon/epoxy composites:moisture uptake[J].Composites Part B,2009,40(1):41-49.
[8] 益小苏,张明,安学锋.先进航空树脂基复合材料研究与应用进展[J].工程塑料应用,2009,37(10):72-76.
[9] 刘代军,陈亚莉.先进树脂基复合材料在航空工业中的应用[J].材料工程,2008(Z1):194-198.
[10] 曲春艳,王德志,冯浩.J-188双马来酰亚胺基复合材料胶接用结构胶膜[J].材料工程,2007(1):15-18.
[11] Hwang H J,Li C H,Wang C S.Die-lectric and thermal properties of dicyclopentadiene containing bismaleimide and cyanate ester.part Ⅳ[J].Polymer,2006,47:1291-1299.
[12] Chartoff R P,Cho J,Carlin P S.Morphology and mechanical properties of rubber modified aromatic-ether bismaleimide matrix resins[J].Polymer Engineering & Science,2010,31(8):563-566.
[13] Shaw S,Kinloch A.Toughened bismaleimide adhesives[J].International Journal of Adhesion & Adhesives,1985,5(3):123-127.
[14] 梁国正,顾盖娟.双马来酰亚胺树脂[M].北京:化学工业出版社,1997:1-2.
[15] Olesen K,Falabella R.Toughened bismaleimide adhesive/primer system and peel ply for aerospace applications[C].US,Los Angeles:40th International SAMPE Symposium,1995:1183-1193.
[16] Manette M,Gebhardt A.Toughened bismaleimide film adhesive for aerospace applications[C].US,Los Angeles:34th International SAMPE Symposium,1989:643-655.
[17] 乔海涛,张宝艳,包建文,等.高韧性双马树脂基胶黏剂的研制[C].北京:第17届全国复合材料学术会议论文集,2012:491-494.
[18] 孟江燕,王云英,向东东,等.湿热环境对T700/5429弯曲和面内压缩强度的影响[J].宇航材料工艺,2012,5:30-33.
[19] 邱军,邹磊,姚秀超.一种改性的双马来酰亚胺树脂胶膜的制备方法:中国,201410369228.8[P].2014-07-30.
[20] 孔宪志,孙东洲,孙禹.一种糊状双马来酰亚胺耐高温胶粘剂的研制[J].化学与粘合,2012,34(1):17-19.
[21] 王超,黄玉东,张斌等.液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂[J].高分子材料科学与工程,2003,19(2):86-88.
[22] 陆逢.碳纳米管和环氧树脂改性双马来酰亚胺树脂的研究[D].武汉:华中科技大学,2015:18-19.
[23] 罗甜.二烯丙基双酚A改性双马来酰亚胺耐高温胶粘剂的研究[D].武汉:武汉理工大学,2010:45-49.
[24] 蓝立文,刘力男.改性双马来酰亚胺胶粘剂的研究[J].粘接,1991,12(2):1-5.
[25] 宋崇健,陆企亭.氰酸酯改性双马来酰亚胺耐高温胶粘剂[C].北京国际粘接技术研讨会暨第二届亚洲粘接技术研讨会论文集,2007:801-806.
[26] 吴广磊,寇开昌,王益群,等,双马来酰亚胺/氰酸酯树脂耐220℃高温胶粘剂及制备方法:中国,201310010829.5[P].2013-05-01.
[27] 杨伏生,周安宁,葛玲梅,等.纳米科技在聚合物改性方面的应用[J].化工进展,2001(8):9-12.
[28] 高其标,申屠宝卿,翁志学.纳米改性聚合物材料研究进展[J].化工生产与技术,2001,8(6):22-26.
[29] 熊艳丽.耐高温双马来酰亚胺型结构胶粘剂的研究[D].西安:西北工业大学,2006:62-72.
[30] 杨海冬,曲春艳,王德志,等.双马来酰亚胺树脂的增韧改性方法:中国,201310460903.3[P].2013-09-30.
[31] 王德志,曲春艳,张杨,等.耐热200℃双马改性环氧结构胶膜的研究[J].中国胶黏剂,2005,14(4):6-9.
[32] 王德志,曲春艳,赵立伟,等.复合材料共胶接双马树脂结构胶膜的研究[C].2013北京国际粘接技术研讨会论文集,2013:15-17.
[33] 陈丽敏,焦婷,雷安民,等.新型双马结构胶J-299性能试验研究[J].科学技术与工程,2014,14(6):97-100.
[34] 王德志,曲春艳,冯浩,等.一种高韧性双马来酰亚胺树脂载体结构胶膜及其制备方法:中国,201310187888.X[P].2014-08-20.
[35] 王德志,曲春艳,冯浩,等.一种耐高温双马来酰亚胺树脂载体结构胶膜及其制备方法:中国,201310187697.3[P].2014-08-20.
[36] 刘长威,王德志,曲春艳,等.一种三分支芳族的丙烯基苯氧基化合物及其制备方法和利用其改性的双马来酰亚胺树脂:中国,201510016943.8[P].2017-01-04.
[37] 刘长威,曲春艳,王德志,等.一种低填充量耐高温导热双马来酰亚胺胶黏剂及其制备方法和胶黏剂的应用:中国,201510016911.8[P].2016-06-08.
基金资助
黑龙江省自然科学基金(JC2017015)
PDF